AISI/SAE 4140 Alloy Steel Bar

AISI/SAE 4140 Alloy Steel Bar Description4140 steel is a 1% chromium-molybdenum general-purpose high-strength steel, usually hardened and tempered in the tensile range of 850-1000 Mpa. 4140 steel has improved machinability, which greatly increases feed and speed, while extend

Factory area 20000 square meters.
Support specification customization.
Strict quality control, ISO certification.
Abide by the contract and deliver on time.
After-sales team gives you the best service.

+86 13293766666

admin@sdyulun.com

Product Details
Comments

AISI/SAE 4140 Alloy Steel Bar Description

4140 steel is a 1% chromium-molybdenum general-purpose high-strength steel, usually hardened and tempered in the tensile range of 850-1000 Mpa. 4140 steel has improved machinability, which greatly increases feed and speed, while extending tool life without affecting mechanical properties. The prehardening and tempering 4140 can be further case hardened by flame or induction hardening and nitriding. AISI4140 steel bars have high strength, hardenability, good toughness, small deformation during quenching, and high creep strength and durable strength at high temperatures.

Product Parameters

Product Name	AISI/SAE 4140 Alloy Steel Bar
Standard	EN/DIN/JIS/ASTM/BS/ASME/AISI, etc.
Common Round Bar Specifications	3.0-50.8 mm, Over 50.8-300mm
Flat Steel Common Specifications	6.35x12.7mm, 6.35x25.4mm, 12.7x25.4mm
Hexagon Bar Common Specifications	AF5.8mm-17mm
Square Bar Common Specifications	AF2mm-14mm, AF6.35mm, 9.5mm, 12.7mm, 15.98mm, 19.0mm, 25.4mm
Length	1-6meters, Size Accept Custom
Diameter(mm)	Hot Rolling Round Bar	25-600	Cold Rolling Square Bar	6-50.8
	Hot Rolling Square Bar	21-54	Cold Rolling Hexagon Bar	9.5-65
	Cold Rolling Round bar	6-101.6	Forged Rebar	200-1000
Surface Process	Bright, Polished, Black
Other Services	Machining(cnc), Centerless Grinding(cg), Heat Treatment, Annealing, Pickling, Polishing, Rolling, Forging, Cutting, Bending, Small Machining, etc.

Chemical Composition

Grade	Mn	S	C	P	Si	Cr	Ni
AISI 4140	0.75-1.00	0.035	0.38-0.43	0.035	0.20-0.35	0.8-1.1	0.15-0.25

Mechanical Properties

Grade	Tensile Strength psi	Yield Strength psi	Elongation %	Hardness HRC
AISI 4140	100k	80k	20	18-22

Scope of Application

SAE 4140 are widely used in most industrial sectors, with a wide range of applications, such as: adapters, spindles, axles, bolts, crankshafts, connecting rods, chuck bodies, chucks, conveyor belt pins and rollers, ejection pins, forks, gears, Guide rods, hydraulic shafts and parts, lathe spindles, logging parts, milling spindles, motor shafts, nuts, clamping rods, various pins, pins, pump shafts, plungers, sleeve, spindle, sprocket, stud bolt, tool holder, torsion bar, worm, etc.