Carbon Steel Coil

4135/4140/4142/6150 Alloy Coil EN10083-3

4135/4140/4142/6150 Alloy Coil EN10083-3 DescriptionThere are steel types 50CrMo4, 51CrV4, 20MnB5, 34CrMo4, 42CrMo4, and 27MnCrB5-2. EN 10083-3 steel coilhas high strength, high toughness and good hardenability. This alloy requires high-temperature preheating before welding to reli

Factory area 20000 square meters.
Support specification customization.
Strict quality control, ISO certification.
Abide by the contract and deliver on time.
After-sales team gives you the best service.

+86 13293766666

admin@sdyulun.com

Product Details
Comments

4135/4140/4142/6150 Alloy Coil EN10083-3 Description

There are steel types 50CrMo4, 51CrV4, 20MnB5, 34CrMo4, 42CrMo4, and 27MnCrB5-2. EN 10083-3 steel coil has high strength, high toughness and good hardenability. This alloy requires high-temperature preheating before welding to relieve stress after welding. EN 10083-3 steel coils are used in the manufacture of tools that require good formability and high strength. It is usually chosen to manufacture large and important parts, such as heavy-duty mechanical shafts, turbine shaft blades, high-load transmission parts, fasteners, crankshafts, gears, and heavy-duty parts of electric motor structures, etc..

Product Parameters

Product Name	4135/4140/4142/6150 Alloy Coil EN10083-3
Production Process	Hot Rolling, Cold Rolling
Material Standards	AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.
Width	45mm-2200mm
Length	Custom Size
Thickness	Hot Rolling: 2.75mm-100mm Cold Rolling: 0.2mm-3mm
Delivery Conditions	Rolling, Annealing, Quenching, Tempered or Standard
Surface Process	Ordinary, Wire Drawing, Laminated Film

Chemical Composition

Brand	C	Si max	Mn	P max	S max	Cr	Mo	V
34CrMo4	0.3-0.37	0.40	0.6-0.9	0.025	0.035	0.9-1.2	0.15-0.3	-
42CrMo4	0.38-0.45	0.40	0.6-0.9	0.025	0.035	0.9-1.2	0.15-0.3	-
50CrMo4	0.46-0.54	0.40	0.5-0.8	0.025	0.035	0.9-1.2	0.15-0.3	-
51CrV4	0.47-0.55	0.40	0.7-1.1	0.025	0.025	0.9-1.2	-	0.1-0.25

Mechanical Properties

Thickness mm	Re min. N/mm2	Rm N/mm2	A min %	From min %	KVb min J
≤ 8	900	1000-1300	10	40	-
8-20	750	1000-1200	11	45	35
20-60	650	900-1100	12	50	35
60-100	550	800-950	13	50	35
100-160	500	750-900	14	55	35

Scope of Application

EN 10083-3 steel plates are used to manufacture tools that require good plasticity and high strength. It is usually selected to manufacture large parts and important parts, such as heavy mechanical shafts, turbine shaft blades, high loads of transmission parts, fasteners, crankshafts, gears, and heavy-duty parts of motor structures.

Equivalent Material

European Standard	American Standard	German Standard	Japanese Standard	National Standard	International Standards
34CrMo4	4135	34CrMo4	SCM435H	35CrMo	34CrMo4
42CrMo4	4140, 4142	42CrMo4	SCM440H	42CrMo	42CrMo4
50CrMo4	-	50CrMo4	-	50CrMo	50CrMo4
51CrV4	6150	50CrV4	SUP10	50CrVA	51CrV4