Carbon Steel Plate

1008 Cold Rolled Steel Plate

1008 Cold Rolled Steel PlateThis alloy is generally used for "commercial quality" cold rolled steel sheet. It is an economical, general purpose steel grade offering moderate strength and toughness. As a standard grade, 1008 steel is used in many common, low-stress a

Factory area 20000 square meters.
Support specification customization.
Strict quality control, ISO certification.
Abide by the contract and deliver on time.
After-sales team gives you the best service.

+86 13293766666

admin@sdyulun.com

Product Details
Comments

1008 Cold Rolled Steel Plate

This alloy is generally used for "commercial quality" cold rolled steel sheet. It is an economical, general purpose steel grade offering moderate strength and toughness. As a standard grade, 1008 steel is used in many common, low-stress applications. Weldability (spot, projection, butt, and fusion) and brazeability are excellent. Applications include extruded, cold headed, cold upset, and cold pressed parts and forms. It has a very good surface finish that is far superior to hot rolled A36.

Product Parameters

Product Name	1008 Cold Rolled Steel Plate
Production Process	Hot Rolling, Cold Rolling
Material Standards	AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.
Width	100mm-3000mm
Length	1m-12m, or Customized Size
Thickness	0.1mm-400mm
Delivery Conditions	Rolling, Annealing, Quenching, Tempered or Standard
Surface Process	Ordinary, Wire Drawing, Laminated Film

Chemical Composition

Element	Content (%)
Iron, Fe	99.31-99.7 %
Manganese, Mn	0.30-0.50 %
Carbon, C	0.10 %
Sulfur, S	0.050 %
Phosphorous, P	0.040 %

Mechanical Properties

Properties	Metric	Imperial
Tensile strength	340 MPa	49300 psi
Yield strength (depending on temper)	285 MPa	41300 psi
Elastic modulus	190-210 Gpa	27557-30458 ksi
Bulk modulus (typical for steel)	200 GPa	29000 ksi
Shear modulus (typical for steel)	80.0 GPa	11600 ksi
Poisson’s ratio	0.27-0.30	0.27-0.30
Elongation at break (in 50 mm)	20 %	20 %
Reduction of area	45 %	45 %
Hardness, Brinell	95	95
Hardness, Knoop (converted from Brinell hardness)	113	113
Hardness, Rockwell B (converted from Brinell hardness)	55	55
Hardness, Vickers (converted from Brinell hardness)	98	98
Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing)	55	55

Scope of Application

AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.