Stainless Steel Bar

330 Stainless Steel Bar

330 Stainless Steel Bar Description330 is an austenitic nickel-chromium-iron-silicon alloy with excellent oxidation and carburizing properties up to 2200 °F and high strength. The high nickel and chromium content of the alloy provides excellent oxidation resistance and carburization, and the silico

Factory area 20000 square meters.
Support specification customization.
Strict quality control, ISO certification.
Abide by the contract and deliver on time.
After-sales team gives you the best service.

+86 13293766666

admin@sdyulun.com

Product Details
Comments

330 Stainless Steel Bar Description

330 is an austenitic nickel-chromium-iron-silicon alloy with excellent oxidation and carburizing properties up to 2200 °F and high strength. The high nickel and chromium content of the alloy provides excellent oxidation resistance and carburization, and the silicon content further improves the oxidation resistance of the alloy. The ultra-high nickel content of 34 to 37% of the alloy 330 also provides high resistance to chloride stress corrosion cracking and embrittlement due to sigma phase precipitation in most furnace atmospheres. The alloy 330 also has a low coefficient of expansion, excellent ductility and high strength.

Product Parameters

Product Name		330 Stainless Steel Bar
Type		Steel Bar
Outer Diameter	Round Bar	4mm-500mm
	Hexagon Bar	18mm-57mm (11/16″ to 2-3/4″)
	Square Bar	18mm-47mm (11/16″ to 1-3/4″)
	Flat Steel	1/2 "to 10", Thickness: 2mm-150mm, Can provide customized
Length		1-6 meters, Length can be customized
Standard		ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface		Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc.
Scope of Application		Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc.

Chemical Composition

C	Si	Mn	Cr	Ni	S	P
≤ 0.08	1.0～1.5	≤ 2.0	18.0～22.0	34.0～37.0	≤ 0.03	≤ 0.03

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥552	≥207	≥ 40	≤ 85HRB

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10^-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(ΜΩ. cm)
8.00	197	14.4	12.5	101.7