Stainless Steel Bar

410 Stainless Steel Bar

410 Stainless Steel Bar Description410 is a basic general-purpose martensitic stainless steel, used for high-stress parts, with good corrosion resistance and high strength and hardness. The alloy 410 contains at least 11.5 percent chromium, which is just enough to exhibit corrosion resistance in mil

Factory area 20000 square meters.
Support specification customization.
Strict quality control, ISO certification.
Abide by the contract and deliver on time.
After-sales team gives you the best service.

+86 13293766666

admin@sdyulun.com

Product Details
Comments

410 Stainless Steel Bar Description

410 is a basic general-purpose martensitic stainless steel, used for high-stress parts, with good corrosion resistance and high strength and hardness. The alloy 410 contains at least 11.5 percent chromium, which is just enough to exhibit corrosion resistance in mild atmospheres, vapors, and many mild chemical environments. It is a general-purpose grade, usually provided in a hardened but still processable condition, for applications that require high strength, medium heat resistance and corrosion resistance. After the 410 is hardened, tempered and polished, it shows the greatest corrosion resistance.

Product Parameters

Product Name		410 Stainless Steel Bar
Type		Steel Bar
Outer Diameter	Round Bar	4mm-500mm
	Hexagon Bar	18mm-57mm (11/16″ to 2-3/4″)
	Square Bar	18mm-47mm (11/16″ to 1-3/4″)
	Flat Steel	1/2 "to 10", Thickness: 2mm-150mm, Can provide customized
Length		1-6 meters, Length can be customized
Standard		ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface		Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc.
Scope of Application		Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc.

Chemical Composition

C	Si	Mn	Cr	Ni	S	P
≤ 0.15	≤ 1.0	≤ 1.0	11.5～13.5	≤ 0.5	≤ 0.03	≤ 0.04

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥450	≥205	≥20	≤ 201HB

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10^-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(ΜΩ. cm)
7.74	200	9.9	24.9	570