317L Stainless Steel Plate

317L Stainless Steel Plate Description317L is a low-carbon austenitic stainless steel containing molybdenum. More chromium, nickel and molybdenum are added to obtain better corrosion resistance and increase the resistance to sulfurous acid, acetic acid, formic acid, citric acid and tartaric acid. Re

Factory area 20000 square meters.
Support specification customization.
Strict quality control, ISO certification.
Abide by the contract and deliver on time.
After-sales team gives you the best service.

+86 13293766666

admin@sdyulun.com

Product Details
Comments

317L Stainless Steel Plate Description

317L is a low-carbon austenitic stainless steel containing molybdenum. More chromium, nickel and molybdenum are added to obtain better corrosion resistance and increase the resistance to sulfurous acid, acetic acid, formic acid, citric acid and tartaric acid. Resistance to chemical attack. Due to its low carbon content, 317L also provides resistance to sensitization during welding, as well as higher creep, rupture stress and high temperature tensile strength. It is non-magnetic in the annealed state, but may become slightly magnetic after welding.

Product Parameters

Product Name	317L Stainless Steel Plate
Type	Plate
Thickness	0.3mm-200mm
Length	2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc.
Width	40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc.
Standard	ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface	BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.
Scope of Application	Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc.
Certificate	ISO, SGS, BV, etc.
Production Technology	Hot Rolling, Cold Rolling
Edge Processing	Edging, Trimming

Chemical Composition

C	Si	Mn	Cr	Ni	S	P	Mo
≤ 0.035	≤ 0.75	≤ 2.0	18.0～20.0	11.0～15.0	≤ 0.03	≤ 0.04	3.0～4.0

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥480	≥177	≥ 40	≤ 187HB;≤ 90HRB;≤ 200HV

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10^-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(ΜΩ. cm)
7.99	193	16.0	16.2	79